Mold experimentation, day 2

Mold 1, side 3 cont:
Demold @ 10h. Mold firm and clean. Part corroded by acetic acid release from RTV.
Mold release failed. If it weren’t for a slight difference in texture and hardness between the molds and the amount of time I spent cleaning up mold side 2 last night, this would be a total loss. As it is, I had to carve apart the mold sides with an exacto.
Detail looks sharp, if dirty,and I think I’ll go for a test run tonight. SDC10017Edit: cast part. Two air bubbles have wrecked it, but the detail is top-notch.